德國拜耳PC/ABS Bayblend FR2000 產品特性：5VA阻燃，尺寸穩定，良好的顏色穩定性，高剛性，耐低溫沖擊，高耐熱性，良好的可加工性，熱穩定性良好，用于家電，汽車應用，草坪和園林設備
我公司提供的產品均為正牌塑膠原料，品質保證，貨源穩定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權威資料請致電13268582149
PC/ABS FR2000 物性表：
| Specific Gravity |
1.18 |
g/cm³ |
ASTM D792 |
| Density |
1180 |
kg/m³ |
ISO 1183 2 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) |
26 |
g/10 min |
ASTM D1238 |
| Melt volume-flow rate (240°C/5.0 kg) |
26.0 |
cm³/10min |
ISO 1133 2 |
| Molding Shrinkage - Flow 3 |
0.50 to 0.70 |
% |
ASTM D955 |
| Molding Shrinkage - Across Flow 3 |
0.50 to 0.70 |
% |
ASTM D955 |
| Water Absorption (Saturation, 23°C, 3.18 mm) |
0.50 |
% |
ISO 62 |
| Water Absorption (Saturation) |
0.50 |
% |
ISO 62 2 |
| Water Absorption (Equilibrium, 23°C, 3.18 mm, 50% RH) |
0.20 |
% |
ISO 62 |
| Water Absorption (Equilibrium) |
0.20 |
% |
ISO 62 2 |
| Spiral Flow Length (254°C, 2.54 mm) |
762 |
mm |
|
| Mechanical |
Nominal Value |
Unit |
Test Method |
| Tensile Modulus 4 (23°C) |
2700 |
MPa |
ASTM D638 |
| Tensile modulus |
2700 |
MPa |
ISO 527-2 2 |
| Tensile Stress (Yield) |
60.0 |
MPa |
ISO 527-2 2 |
| Tensile Strength 5 (Break, 23°C) |
44.8 |
MPa |
ASTM D638 |
| Tensile Elongation 5 (Yield, 23°C) |
4.0 |
% |
ASTM D638 |
| Tensile Strain (Yield) |
4.0 |
% |
ISO 527-2 2 |
| Tensile Elongation 5 (Break, 23°C) |
> 50 |
% |
ASTM D638 |
| Nominal strain at break |
> 50 |
% |
ISO 527-2 2 |
| Flexural Modulus (23°C) |
2690 |
MPa |
ASTM D790 |
| Flexural Strength (5.0% Strain, 23°C) |
95.1 |
MPa |
ASTM D790 |
| Impact |
Nominal Value |
Unit |
Test Method |
| Notched Izod Impact (23°C, 3.18 mm) |
430 |
J/m |
ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) |
No Break |
|
ASTM D4812 |
| Thermal |
Nominal Value |
Unit |
Test Method |
| Deflection Temperature Under Load (0.45 MPa) |
90.0 |
°C |
ISO 75-2 2 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) |
82.2 |
°C |
ASTM D648 |
| Deflection Temperature Under Load (1.8 MPa) |
80.0 |
°C |
ISO 75-2 2 |
| Vicat Softening Temperature |
95.0 |
°C |
ASTM D1525 6 |
| Vicat Softening Temperature (50°C/h, B (50N)) |
92.0 |
°C |
ISO 306 2 |
| CLTE - Flow |
0.000077 |
cm/cm/°C |
ASTM D696 |
| CLTE - Flow |
0.000076 |
cm/cm/°C |
ISO 11359-2 2 |
| CLTE - Transverse |
0.000077 |
cm/cm/°C |
ASTM D696 |
| CLTE - Transverse |
0.000080 |
cm/cm/°C |
ISO 11359-2 2 |
| Electrical |
Nominal Value |
Unit |
Test Method |
| Surface Resistivity |
1.0E+16 |
ohms |
IEC 60093 |
| Volume Resistivity (23°C) |
1.0E+16 |
ohm·cm |
IEC 60093 |
| Relative Permittivity (100 Hz) |
3.20 |
|
IEC 60250 2 |
| Relative Permittivity (1 MHz) |
3.10 |
|
IEC 60250 2 |
| Relative Permittivity |
|
|
IEC 60250 |
| 23°C, 100 Hz |
3.20 |
|
|
| 23°C, 1 MHz |
3.10 |
|
|
| Dissipation Factor |
|
|
IEC 60250 |
| 23°C, 100 Hz |
0.0050 |
|
|
| 23°C, 1 MHz |
0.0070 |
|
|
| Dissipation Factor (100 Hz) |
0.0050 |
|
IEC 60250 2 |
| Dissipation Factor (1 MHz) |
0.0070 |
|
IEC 60250 2 |
| Comparative Tracking Index (Solution A) |
400 |
V |
IEC 60112 |
| Comparative tracking index |
500 |
|
IEC 60112 2 |
| Electric Strength (23°C) |
30 |
kV/mm |
IEC 60243-1 |
| Electric strength |
30 |
kV/mm |
IEC 60243-1 2 |
| Flammability |
Nominal Value |
Unit |
Test Method |
| Flame Rating - UL |
|
|
UL 94 |
| 2.00 mm |
5VB |
|
|
| 3.00 mm |
5VA |
|
|
PC/ABS 韓國LG EC-5000AF 通用注塑級
PC/ABS 韓國LG EU-5000 通用注塑級
PC/ABS 韓國LG EU-5000G 通用注塑級
PC/ABS 韓國LG EU-5007 通用注塑級
PC/ABS 韓國LG GN-5001RF 通用注塑級 注射成型
PC/ABS 韓國LG GN-5001SF-NP 通用注塑級
PC/ABS 韓國LG GN-5001TF 通用注塑級
PC/ABS 韓國LG GN-5007FM 通用注塑級
PC/ABS 韓國LG GN-5008HF 通用注塑級
PC/ABS 韓國LG GN-5009F 通用注塑級 阻燃
PC/ABS 韓國LG GN-5101RF 通用注塑級
PC/ABS 韓國LG GN-5151RFA 通用注塑級
PC/ABS 韓國LG GN-5151RFH 通用注塑級
PC/ABS 韓國LG GN-5301F 通用注塑級
PC/ABS 韓國LG GP-5008BF 通用注塑級
PC/ABS 韓國LG GP-5008BFH 通用注塑級
PC/ABS 韓國LG GP-5200 通用注塑級
PC/ABS 韓國LG GP-5206F 通用注塑級
PC/ABS 韓國LG GP-5300 通用注塑級
PC/ABS 韓國LG HI-5002A 通用注塑級
PC/ABS 韓國LG HR-5006A 通用注塑級
PC/ABS 韓國LG HR-5007A 通用注塑級
PC/ABS 韓國LG HR-5007AX 通用注塑級