點擊圖片查看大圖- POM/107UV/美國杜邦
- 生產(chǎn)企業(yè)： 美國杜邦
| 規(guī)格級別 | 注塑 | 外觀顏色 | |
| 該料用途 | |||
| 備注說明 | 特性：均聚甲醛，強度、剛度、熱穩(wěn)定性能好、硬度好。 | ||
| 加工條件 |
③原料技術(shù)數(shù)據(jù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 其它性能 | 彎曲降服強度 | +73℉ | ASTM D-790 | 14.3 | MPsi |
| 基本性能 | 密度 | ASTM D-792 | 1.42 | ||
| 物理性能 | 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D-570 | 0.22 | % |
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D-570 | 0.25 | % | |
| 吸水量 | 浸泡均衡點+73℉(+23℃) | ASTM D-570 | 0.90 | % | |
| 擴散因數(shù) | +73℉(+23℃)106Hz | ASTM D-150 | 0.005 | ||
| 機械性能 | 摩擦系數(shù) | +73℉(+23℃)動態(tài) | ThrustWasherTest3 | 0.35 | |
| 撓曲系數(shù) | +70℃ | 在25℃下 | 1550 | MPa | |
| 撓曲系數(shù) | -55℃ | 在25℃下 | 3650 | MPa | |
| 斷裂時之拉力伸張度 | +73℉(+23℃) | ASTM D-638 | 75 | % | |
| 撓曲系數(shù) | +158℉ | 在25℃下 | 225 | MPsi | |
| 伸張強度 | +212℉ | ASTM D-638 | 5.2 | MPsi | |
| 斷裂時之拉力伸張度 | +212℉(+100℃) | ASTM D-638 | >260 | % | |
| IZOD沖擊強度 | +73℉ | ASTM D-256 | 2.3 | ft.lb/in | |
| 伸張強度 | +250℉ | ASTM D-638 | 3.8 | MPsi | |
| 伸張強度 | -68℉ | ASTM D-638 | 14.7 | MPsi | |
| 撓曲系數(shù) | +212℉ | 在25℃下 | 130 | MPsi | |
| 撓曲系數(shù) | -68℉ | 在25℃下 | 530 | MPsi | |
| 撓曲系數(shù) | +250℉ | 在25℃下 | 90 | MPsi | |
| 拉力沖擊抵抗力 | +73℉ | D1822Long | 170 | ft.lb/in2 | |
| 拉力沖擊抵抗力 | +23℃ | D1822Long | 350 | kj/m2 | |
| 剪力 | +23℃ | ASTM D-732 | 65.5 | MPa | |
| 撓曲系數(shù) | +73℉ | 在25℃下 | 380 | MPsi | |
| 剪力 | +73℉ | ASTM D-732 | 9.5 | MPsi | |
| 撓曲系數(shù) | +100℃ | 25℃下 | 895 | MPa | |
| 彎曲疲勞忍耐限度 | +73℉ | ASTM D-671 | 4.7 | MPsi | |
| 伸張強度 | +100℃ | ASTM D-638 | 35.9 | MPa | |
| 斷裂時之拉力伸張度 | +250℉(+122℃) | ASTM D-638 | >260 | % | |
| 斷裂時之拉力伸張度 | +158℉(+70℃) | ASTM D-638 | 230 | % | |
| 無切口沖擊程度 | +73℉ | ASTM D-256 | >100(no break) | ft.lb/in | |
| 彎曲降服強度 | +23℃ | ASTM D-790 | 98.6 | MPa | |
| 壓縮應(yīng)力 | +23℃@1%Def. | ASTM D-695 | 35.9 | MPa | |
| 伸張強度 | -55℃ | ASTM D-638 | 101 | MPa | |
| 撓曲系數(shù) | +23℃ | 在25℃下 | 2620 | MPa | |
| 伸張強度 | +73℉ | ASTM D-638 | 10.0 | MPsi | |
| 壓縮應(yīng)力 | +73℉@10%Def | ASTM D-695 | 18.0 | MPsi | |
| 伸張強度 | +122℃ | ASTM D-638 | 26.2 | MPa | |
| 壓縮應(yīng)力 | +23℃@10%Def. | ASTM D-695 | 124 | MPa | |
| 伸張強度 | +70℃ | ASTM D-638 | 6.9 | MPa | |
| 彎曲疲勞忍耐限度 | +23℃ | ASTM D-671 | 32.4 | MPa | |
| IZOD沖擊強度 | 40℃ | ASTM D-256 | 96.1 | j/m | |
| 伸張強度 | +158℉ | ASTM D-638 | 6.9 | MPsi | |
| IZOD沖擊強度 | -40℉ | ASTM D-256 | 1.8 | ft.lb/in | |
| 洛氏硬度 | ASTM D-785 | M94,R120 | |||
| 撓曲系數(shù) | +122℃ | 在25℃下 | 620 | MPa | |
| 彈性系數(shù) | +73℉ | ASTM D-638 | 450 | MPsi | |
| 摩擦系數(shù) | +73℉(+23℃)靜態(tài) | ThrustWasherTest3 | 0.20 | ||
| 彈性系數(shù) | +23℃ | ASTM D-638 | 3100 | MPa | |
| 斷裂時之拉力伸張度 | -68℉(-55℃) | ASTM D-638 | 38 | % | |
| 負載下之變形 | 2000psi@+122℉(14Mpa@50℃) | ASTM D-621 | 0.5 | % | |
| 伸張強度 | +23℃ | ASTM D-638 | 68.9 | MPa | |
| 無切口沖擊程度 | +23℃ | ASTM D-256 | >5300(no break) | j/m | |
| IZOD沖擊強度 | +23℃ | ASTM D-256 | 123 | j/m | |
| 壓縮應(yīng)力 | +73℉@1%Def. | ASTM D-695 | 5.2 | MPsi | |
| 電氣性能 | 絕緣強度 | Short Time,2.3mm | ASTM D-149 | 19.7 | MV/m |
| 絕緣系數(shù) | +73℉(+23℃)102to106Hz | ASTM D-150 | 3.7 | ||
| 電弧抵抗力 | 120mil(3.1mm) | ASTM D-495 | 220no tracking | Sec. | |
| 絕緣強度 | Short Time,90 mils | ASTM D-149 | 500 | V/mil | |
| 電阻系數(shù) | +73℉(+23℃)0.2%H2O | ASTM D-257 | 1015 | ohm-cm | |
| 熱性能 | 可燃燒性 | UL-94 | 94HB | ||
| 線性熱膨脹系數(shù) | -40 to +85℉ | ASTM D-696 | 5.8 | 10-5in/in.℉ | |
| 線性熱膨脹系數(shù) | +220 to +300℉ | ASTM D-696 | 8.3 | 10-5in/in.℉ | |
| 熱變形溫度 | 0.5MPa | ASTM D-648 | 172 | ℃ | |
| 線性熱膨脹系數(shù) | -40 to +29℃ | ASTM D-696 | 10.4 | 10-5m/m.℃ | |
| 熱傳導(dǎo)系數(shù) | 2.6 | BTU-in/hr | |||
| 線性熱膨脹系數(shù) | +60 to +104℃ | ASTM D-696 | 13.7 | 10-5m/m.℃ | |
| 熱變形溫度 | 1.8MPa | ASTM D-648 | 136 | ℃ | |
| 熱變形溫度 | 66psi | ASTM D-648 | 342 | ℉ | |
| 熔點 | ASTM D-2133 | 175 | ℃ | ||
| 熱變形溫度 | 264psi | ASTM D-648 | 277 | ℉ | |
| 熔點 | ASTM D-2133 | 347 | ℉ | ||
| 線性熱膨脹系數(shù) | +29 to +60℃ | ASTM D-696 | 12.2 | 10-5m/m.℃ | |
| 線性熱膨脹系數(shù) | +104 to +150℃ | ASTM D-696 | 14.9 | 10-5m/m.℃ | |
| 線性熱膨脹系數(shù) | +85 to +140℉ | ASTM D-696 | 6.8 | 10-5in/in.℉ | |
| 線性熱膨脹系數(shù) | +140 to +220℉ | ASTM D-696 | 7.6 | 10-5in/in.℉ | |
| 熱傳導(dǎo)系數(shù) | 0.37 | W/mk | |||